我公司可生产ASTM A252 高强度低合金铌-钒结构钢

钢管材质等级为ASTM A572 GR.42、ASTM A572 GR.50、ASTM A572 GR.55、ASTM A572 GR.60、ASTM A572 GR.65

一、ASTM A572直缝钢管力学性能和化学成分（仅限于SAWL直缝钢管）

ASTM A572直缝钢管力学性能

ASTM A572 GR.42

屈服强度≥290MPa，抗拉强度≥415MPa，标距8英寸伸长率≥20%

ASTM A572 GR.50

屈服强度≥345MPa，抗拉强度≥450MPa，标距8英寸伸长率≥18%

ASTM A572 GR.55

屈服强度≥380MPa，抗拉强度≥485MPa，标距8英寸伸长率≥17%

ASTM A572 GR.60

屈服强度≥415MPa，抗拉强度≥520MPa，标距8英寸伸长率≥16%

ASTM A572 GR.65

屈服强度≥450MPa，抗拉强度≥550MPa，标距8英寸伸长率≥15%

 

 

ASTM A572直缝钢管化学成分

ASTM A572GR.42

碳≤0.21%，锰≤1.35%，磷≤0.04%，硫≤0.05%，硅≤0.40%

ASTM A572GR.50

碳≤0.23%，锰≤1.35%，磷≤0.04%，硫≤0.05%，硅≤0.40%

ASTM A572GR.55

碳≤0.25%，锰≤1.35%，磷≤0.04%，硫≤0.05%，硅≤0.40%

ASTM A572GR.60

碳≤0.26%，锰≤1.35%，磷≤0.04%，硫≤0.05%，硅≤0.40%

ASTM A572GR.65（厚度≤13mm）

碳≤0.23%，锰≤1.65%，磷≤0.04%，硫≤0.05%，硅≤0.40%

ASTM A572GR.65（厚度>13-32mm）

碳≤0.26%，锰≤1.35%，磷≤0.04%，硫≤0.05%，硅≤0.40%

 

ASTM A572 铌钒合金含量（熔炼分析）

1类：铌≤0.005-0.05%

2类：钒≤0.01-0.15%

3类：铌≤0.005-0.05%，钒≤0.01-0.15%，铌+钒≤0.02-0.15%

5类：钛≤0.006-0.04%，氮≤0.003-0.015%，钒≤0.06%

 

二、ASTMA572直缝钢管公差（参考ASTM A500碳素结构钢管生产规范）

ASTMA572直缝钢管外径公差（外径≥50.8mm）

实际外径与规定外径的公差为±0.75%，精确到0.13mm

ASTMA572直缝钢管壁厚公差

实际壁厚和规定壁厚的公差为±10%

ASTMA572直缝钢管长度公差

定尺长度小于等于6.7米，公差为-6.4mm+12.7mm

定尺长度6.7-13.4m（不含6.7米含13.4米）公差为-6.4mm+19mm

ASTMA572直缝钢管直度公差

直度公差≤10.4mm乘以长度m除以5（直度=10.4*L/5）

三、我公司对ASTMA572直缝埋弧焊钢管的无损检测试验：

射线和超声检测（RT&UT）

射线（RT）：100%钢管进行全程射线检测

超声（UT）：100%钢管进行全程超声检测

 

四、ASTM A572国内用什么材质替代

ASTM A572 GR.42、ASTM A572 GR.50、ASTM A572 GR.55、ASTM A572 GR.60.、ASTM A572 GR.65

用什么材质代替

ASTM A572 GR.42用国内什么材质代替

ASTM A572 GR.42用国标Q345B/C/D（屈服强度345MPa，抗拉强度470-630MPa）

ASTM A572 GR.50用国内什么材质代替

ASTM A572 GR.50用国标Q345B/C/D（屈服强度345MPa，抗拉强度470-630MPa）

ASTM A572 GR.55用国内什么材质代替

ASTM A572 GR.55用国标Q390B/C/D（屈服强度390MPa，抗拉强度490-650MPa）

ASTM A572 GR.60用国内什么材质代替

ASTM A572 GR.60用国标Q420B/C/D（屈服强度420MPa，抗拉强度520-680MPa）

ASTM A572 GR.65用国内什么材质代替

ASTM A572 GR.65用国标Q460C/D/E（屈服强度460MPa，抗拉强度550-720MPa）